SABIC Innovative Plastics LNP Verton RV008ESV PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Shanghai port, China
Download PDF SABIC Innovative Plastics LNP Verton RV008ESV PA 66.pdf
Price EMAIL US  sales@lookpolymers.com
Material Notes:
40% long glass fiber filled PA66 Verton Xtreme XCThis data was supplied by SABIC-IP for the Americas region.
Mechanical Properties Metric English Comments
Density 1.498 g/cc
0.05412 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 1.1 %
1.1 %
23°C / 50% RH; ISO 62
0.72 %
<br>@Time 86400 sec
 0.72 %
<br>@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
<br>@Time 86400 sec
 0.0020 in/in
<br>@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm
<br>@Time 86400 sec
 0.0080 in/in
<br>@Time 24.0 hour
 ASTM D 955
Thermal Properties Metric English Comments
Tensile Strength at Break 207 MPa
30000 psi
Type I, 5 mm/min; ASTM D 638
209 MPa
30300 psi
5 mm/min; ISO 527
Tensile Strength, Yield 207 MPa
30000 psi
Type I, 5 mm/min; ASTM D 638
208 MPa
30200 psi
5 mm/min; ISO 527
Elongation at Break 1.8 %
1.8 %
5 mm/min; ISO 527
1.9 %
1.9 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 1.8 %
1.8 %
5 mm/min; ISO 527
1.9 %
1.9 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 14.06 GPa
2039 ksi
1 mm/min; ISO 527
14.06 GPa
2039 ksi
50 mm/min; ASTM D 638
Flexural Strength 285 MPa
41300 psi
2 mm/min; ISO 178
Flexural Yield Strength 288 MPa
41800 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 10.3 GPa
1490 ksi
1.3 mm/min, 50 mm span; ASTM D 790
10.57 GPa
1533 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.07 J/cm
<br>@Temperature 23.0 °C
 3.88 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 11.4 J/cm
<br>@Temperature 23.0 °C
 21.4 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 18.0 kJ/m²
<br>@Temperature 23.0 °C
 8.57 ft-lb/in²
<br>@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 73.0 kJ/m²
<br>@Temperature 23.0 °C
 34.7 ft-lb/in²
<br>@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 7.00 J
<br>@Temperature 23.0 °C
 5.16 ft-lb
<br>@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Optical Properties Metric English Comments
CTE, linear, Parallel to Flow 26.0 - 28.0 µm/m-°C
<br>@Temperature -30.0 - 30.0 °C
 14.4 µin/in-°F
<br>@Temperature -22.0 - 86.0 °F
 ASTM E 831
CTE, linear, Transverse to Flow 63.0 - 65.0 µm/m-°C
<br>@Temperature -30.0 - 30.0 °C
 35.0 µin/in-°F
<br>@Temperature -22.0 - 86.0 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 259 °C
498 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
254 °C
<br>@Thickness 3.20 mm
 489 °F
<br>@Thickness 0.126 in
 unannealed; ASTM D 648