DuPont Performance Polymers Zytel® HTN FR52G20NH BK337 Polyphthalamide (PPA)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN FR52G20NH BK337 Polyphthalamide (PPA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® HTNFR52G20NH BK337 is a 20% glass reinforced, flame retardant, lubricated high performance polyamide resin. It is also a PPA resin and it uses a non-halogenated flame retardant.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
DAM; ISO 1183
Filler Content 20 %
20 %
DAM
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 2.00 mm
 0.0030 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Thickness 2.00 mm
 0.011 in/in

@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 123 MPa

@Temperature 23.0 °C
 17800 psi

@Temperature 73.4 °F
 50%RH; ISO 527
135 MPa

@Temperature 23.0 °C
 19600 psi

@Temperature 73.4 °F
 DAM; ISO 527
Tensile Stress 4.06 MPa

@Strain 0.100 %,
Temperature 150 °C
 589 psi

@Strain 0.100 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
4.48 MPa

@Strain 0.100 %,
Temperature 150 °C
 650 psi

@Strain 0.100 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
4.84 MPa

@Strain 0.100 %,
Temperature 100 °C
 702 psi

@Strain 0.100 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
5.83 MPa

@Strain 0.100 %,
Temperature 100 °C
 846 psi

@Strain 0.100 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
6.42 MPa

@Strain 0.100 %,
Temperature 60.0 °C
 931 psi

@Strain 0.100 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
7.74 MPa

@Strain 0.200 %,
Temperature 150 °C
 1120 psi

@Strain 0.200 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
8.03 MPa

@Strain 0.100 %,
Temperature 80.0 °C
 1160 psi

@Strain 0.100 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
8.52 MPa

@Strain 0.100 %,
Temperature 40.0 °C
 1240 psi

@Strain 0.100 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
8.59 MPa

@Strain 0.200 %,
Temperature 150 °C
 1250 psi

@Strain 0.200 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
8.69 MPa

@Strain 0.100 %,
Temperature 60.0 °C
 1260 psi

@Strain 0.100 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
9.25 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 1340 psi

@Strain 0.100 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
9.29 MPa

@Strain 0.100 %,
Temperature 23.0 °C
 1350 psi

@Strain 0.100 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
9.36 MPa

@Strain 0.200 %,
Temperature 100 °C
 1360 psi

@Strain 0.200 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
10.29 MPa

@Strain 0.100 %,
Temperature -40.0 °C
 1492 psi

@Strain 0.100 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
11.07 MPa

@Strain 0.300 %,
Temperature 150 °C
 1606 psi

@Strain 0.300 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
11.24 MPa

@Strain 0.200 %,
Temperature 100 °C
 1630 psi

@Strain 0.200 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
12.37 MPa

@Strain 0.200 %,
Temperature 60.0 °C
 1794 psi

@Strain 0.200 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
12.41 MPa

@Strain 0.300 %,
Temperature 150 °C
 1800 psi

@Strain 0.300 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
13.53 MPa

@Strain 0.300 %,
Temperature 100 °C
 1962 psi

@Strain 0.300 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
14.54 MPa

@Strain 0.400 %,
Temperature 150 °C
 2109 psi

@Strain 0.400 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
15.44 MPa

@Strain 0.200 %,
Temperature 80.0 °C
 2239 psi

@Strain 0.200 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
16.31 MPa

@Strain 0.400 %,
Temperature 150 °C
 2366 psi

@Strain 0.400 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
16.5 MPa

@Strain 0.200 %,
Temperature 40.0 °C
 2390 psi

@Strain 0.200 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
16.51 MPa

@Strain 0.300 %,
Temperature 100 °C
 2395 psi

@Strain 0.300 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
16.93 MPa

@Strain 0.200 %,
Temperature 60.0 °C
 2455 psi

@Strain 0.200 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
17.68 MPa

@Strain 0.500 %,
Temperature 150 °C
 2564 psi

@Strain 0.500 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
17.87 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 2592 psi

@Strain 0.200 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
17.89 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 2595 psi

@Strain 0.200 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
17.91 MPa

@Strain 0.400 %,
Temperature 100 °C
 2598 psi

@Strain 0.400 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
18.12 MPa

@Strain 0.300 %,
Temperature 60.0 °C
 2628 psi

@Strain 0.300 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
19.7 MPa

@Strain 0.500 %,
Temperature 150 °C
 2860 psi

@Strain 0.500 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
19.81 MPa

@Strain 0.200 %,
Temperature -40.0 °C
 2873 psi

@Strain 0.200 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
20.61 MPa

@Strain 0.600 %,
Temperature 150 °C
 2989 psi

@Strain 0.600 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
21.72 MPa

@Strain 0.500 %,
Temperature 100 °C
 3150 psi

@Strain 0.500 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
22.17 MPa

@Strain 0.400 %,
Temperature 100 °C
 3215 psi

@Strain 0.400 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
22.5 MPa

@Strain 0.300 %,
Temperature 80.0 °C
 3260 psi

@Strain 0.300 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
22.87 MPa

@Strain 0.600 %,
Temperature 150 °C
 3317 psi

@Strain 0.600 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
23.27 MPa

@Strain 0.700 %,
Temperature 150 °C
 3375 psi

@Strain 0.700 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
24.19 MPa

@Strain 0.400 %,
Temperature 60.0 °C
 3508 psi

@Strain 0.400 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
24.21 MPa

@Strain 0.300 %,
Temperature 40.0 °C
 3511 psi

@Strain 0.300 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2
24.71 MPa

@Strain 0.300 %,
Temperature 60.0 °C
 3584 psi

@Strain 0.300 %,
Temperature 140 °F
 DAM; ISO 11403-1/-2
25.3 MPa

@Strain 0.600 %,
Temperature 100 °C
 3670 psi

@Strain 0.600 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
25.78 MPa

@Strain 0.800 %,
Temperature 150 °C
 3739 psi

@Strain 0.800 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
25.83 MPa

@Strain 0.700 %,
Temperature 150 °C
 3746 psi

@Strain 0.700 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
26.01 MPa

@Strain 0.300 %,
Temperature 23.0 °C
 3772 psi

@Strain 0.300 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
26.13 MPa

@Strain 0.300 %,
Temperature 23.0 °C
 3790 psi

@Strain 0.300 %,
Temperature 73.4 °F
 DAM; ISO 11403-1/-2
27.0 MPa

@Strain 0.500 %,
Temperature 100 °C
 3920 psi

@Strain 0.500 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
28.2 MPa

@Strain 0.900 %,
Temperature 150 °C
 4090 psi

@Strain 0.900 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
28.59 MPa

@Strain 0.800 %,
Temperature 150 °C
 4147 psi

@Strain 0.800 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
28.7 MPa

@Strain 0.300 %,
Temperature -40.0 °C
 4160 psi

@Strain 0.300 %,
Temperature -40.0 °F
 DAM; ISO 11403-1/-2
28.76 MPa

@Strain 0.700 %,
Temperature 100 °C
 4171 psi

@Strain 0.700 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
29.54 MPa

@Strain 0.500 %,
Temperature 60.0 °C
 4284 psi

@Strain 0.500 %,
Temperature 140 °F
 50%RH; ISO 11403-1/-2
29.86 MPa

@Strain 0.400 %,
Temperature 80.0 °C
 4331 psi

@Strain 0.400 %,
Temperature 176 °F
 DAM; ISO 11403-1/-2
30.47 MPa

@Strain 1.00 %,
Temperature 150 °C
 4419 psi

@Strain 1.00 %,
Temperature 302 °F
 50%RH; ISO 11403-1/-2
31.22 MPa

@Strain 0.900 %,
Temperature 150 °C
 4528 psi

@Strain 0.900 %,
Temperature 302 °F
 DAM; ISO 11403-1/-2
31.5 MPa

@Strain 0.600 %,
Temperature 100 °C
 4570 psi

@Strain 0.600 %,
Temperature 212 °F
 DAM; ISO 11403-1/-2
31.93 MPa

@Strain 0.800 %,
Temperature 100 °C
 4631 psi

@Strain 0.800 %,
Temperature 212 °F
 50%RH; ISO 11403-1/-2
32.21 MPa

@Strain 0.400 %,
Temperature 40.0 °C
 4672 psi

@Strain 0.400 %,
Temperature 104 °F
 50%RH; ISO 11403-1/-2