Plastcom SLOVALEN PC 51 C 30 Polypropylene Homopolymer and Copolymer, 30% Micronized Talc

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 30% Talc Filler
Manufacturer	Plastcom spol. s r.o.
Trade Name	SLOVALEN
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom SLOVALEN PC 51 C 30 Polypropylene Homopolymer and Copolymer, 30% Micronized Talc.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FeaturesModified homopolymer and copolymer PP for injection moulding with the content of 30% micronized, chemically modified talc. Increased strength, rigidity and thermal application up to 120°C. Decreased shrinkage. Packing material, garden flower-pots, toys, dowels, clamps, hinge, office chairs, holders, covers of motors, chassis, protection trims in the automotive industry, electroinstallation boxes in the electrical industry. Fulfills the glow wire 750°C. Delivered in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³	STN 64 0111
Linear Mold Shrinkage	0.0178 cm/cm	0.0178 in/in	STN 64 0808
Linear Mold Shrinkage, Transverse	0.0191 cm/cm	0.0191 in/in	STN 64 0808
Melt Flow	5.0 g/10 min @Load 2.16 kg, Temperature 230 °C	5.0 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	25.0 MPa	3630 psi	STN EN ISO 527-2
Elongation at Break	4.0 %	4.0 %	STN EN ISO 527-2
Tensile Modulus	1.70 GPa	247 ksi	STN EN ISO 527-2
Flexural Strength	30.0 MPa	4350 psi	STN EN ISO 178
Flexural Modulus	1.50 GPa	218 ksi	STN EN ISO 178
Charpy Impact Unnotched	2.10 J/cm² @Temperature -20.0 °C	9.99 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	4.50 J/cm² @Temperature 23.0 °C	21.4 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179
Charpy Impact, Notched	0.200 J/cm² @Temperature -20.0 °C	0.952 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	0.400 J/cm² @Temperature 23.0 °C	1.90 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	160 °C	320 °F	DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	110 °C	230 °F	STN EN ISO 75/A
Vicat Softening Point	154 °C	309 °F	B; STN EN ISO 306

Processing Properties	Metric	English
Melt Temperature	200 - 250 °C	392 - 482 °F
Mold Temperature	40.0 - 70.0 °C	104 - 158 °F
Injection Pressure	70.0 - 120 MPa	10200 - 17400 psi