SABIC Innovative Plastics LNP Thermocomp RFZ349 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RFZ349 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RFZ349 is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0119 cm/cm @Time 86400 sec |
0.0119 in/in @Time 24.0 hour |
ISO 294 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| 124 MPa | 18000 psi | ASTM D 638 | |
| Elongation at Break | 2.3 % | 2.3 % | ASTM D 638 |
| 3.2 % | 3.2 % | ISO 527 | |
| Tensile Modulus | 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D 638 |
| 11.4 GPa | 1650 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D 790 |
| 197 MPa | 28600 psi | ISO 178 | |
| Flexural Modulus | 7.17 GPa | 1040 ksi | ASTM D 790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.87 J/cm @Temperature 23.0 °C |
11.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² @Temperature 23.0 °C |
18.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 237 °C @Thickness 3.20 mm |
459 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Prodways PLASTCure ABS 3650 3D Printing Polymer
- Imerys Minsparâ„¢ 170 Feldspar
- Kinlead HSD12 Normal Grade Heat Sealable Film (thickness: 20 µm)
- Teknor Apex MONPRENE® MP 2825E Thermoplastic Elastomer
- Teknor Apex Telcar® TL-1035-70UV Thermoplastic Elastomer
- DSM Akulon® F132-E2 PA6
- Chicago Extruded Metals BioBrass® UNS C62500 Aluminum Bronze
- Beijing Chemical Industry KAIFA® 301-G15F PBT Resin
- DuPont Performance Polymers Neoprene NPR-9368 Polychloroprene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved