SABIC Innovative Plastics Cycoloy® C6200 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C6200 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 14.5 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 14.5 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Spiral Flow 68.58 cm

@Temperature 260 °C
 27.00 in

@Temperature 500 °F
 10 ips,3.175 X 1524 mm
Mechanical Properties Metric English Comments
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 50 %
50 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 103 MPa
14900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 2.68 GPa
389 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
ASTM D256
Dart Drop, Total Energy 61.0 J
45.0 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
54.0 J

@Temperature -30.0 °C
 39.8 ft-lb

@Temperature -22.0 °F
 Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 unannealed; ASTM D648
90.0 °C

@Thickness 6.40 mm
 194 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.710 mm
 HB

@Thickness 0.0280 in
 UL 94
V-1

@Thickness 1.21 mm
 V-1

@Thickness 0.0476 in
 UL 94
V-0

@Thickness 1.47 mm
 V-0

@Thickness 0.0579 in
 UL 94
5VB

@Thickness 2.00 mm
 5VB

@Thickness 0.0787 in
 UL 94
5VA

@Thickness 3.40 mm
 5VA

@Thickness 0.134 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
 2.7

@Frequency 1.00e+6 Hz
 IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
 2.8

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
 432 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
 635 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
 889 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.0040

@Frequency 50.0 - 60.0 Hz
 0.0040

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0080

@Frequency 1.00e+6 Hz
 0.0080

@Frequency 1.00e+6 Hz
 IEC 60250
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A