Lehmann & Voss LUVOCOM® 1301-7578 PPS, linear, with glass fiber and PTFE, improved wear resistance
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-7578 PPS, linear, with glass fiber and PTFE, improved wear resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts with low creep.Improved friction and wear behaviour. Emergency running property.High chemical resistance parts.Control disks, gear wheels, pump impellers, gear parts for automotive appliances, chip carrier.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.83 g/cc | 1.83 g/cc | ISO 1183 |
| Water Absorption | <= 0.050 % | <= 0.050 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 110 MPa | 16000 psi | |
| Elongation at Yield | 1.0 % | 1.0 % | |
| 1.4 % | 1.4 % | flexural | |
| Modulus of Elasticity | 15.0 GPa | 2180 ksi | |
| Flexural Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 13.0 GPa | 1890 ksi | |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.0 µm/m-°C | 12.8 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (beige) |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 W 40 Polyamide 66, 40% Mineral Filled
- Fiberfil® PP-61/TC/20/UV Polypropylene Copolymer, 20% Talc, UV Stabilized
- Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled
- Kingfa PA6-M25G20 20% Glass & 25% Mineral Filled PA6
- SABIC Innovative Plastics NORYL SE1GFN3 PPE+HIPS (Europe-Africa-Middle East)
- Samsung Cheil Industries Infino® HN-3203G PC, Glass Filled FR
- Thermoseal KLINGERSIL® C-5400 Neoprene Gasketing
- Weartech International WT Ni-60 Nickel Hardfacing & Wear Resistant Alloy
- 3M 5010 Polyurethane Multi-Purpose Adhesive
Copyright © lookpolymers.com All Rights Reserved