SABIC Innovative Plastics LNP THERMOTUF PX95726 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF PX95726 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* PX95726 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Moisture Absorption | 1.10 % | 1.10 % | 50% RH, 24 hrs; ASTM D570 |
| 1.60 % | 1.60 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm @Time 86400 sec |
0.0080 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 107 MPa | 15500 psi | ASTM D638 | |
| 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 109 MPa | 15800 psi | 5 mm/min; ISO 527 |
| 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D638 |
| 3.8 % | 3.8 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.79 GPa | 840 ksi | 1 mm/min; ISO 527 |
| 5.83 GPa | 846 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| 170 MPa | 24700 psi | ASTM D790 | |
| Flexural Yield Strength | 173 MPa | 25100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.79 GPa | 695 ksi | 2 mm/min; ISO 178 |
| 4.96 GPa | 719 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 5.03 GPa | 730 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.670 J/cm | 1.26 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.76 J/cm | 16.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 44.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
24.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 138 µm/m-°C @Temperature -30.0 - 30.0 °C |
76.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 148 (SO) Synthetic Oil
- SABIC Innovative Plastics Lexan® HPS1S PC
- Karina Karintox 70/2 Polyolefin Compound
- Kolon ELLAS K-793AB Ester Based Thermoplastic Polyurethane
- Lubriplate SYN LUBE 320 PAO-Based Multi-Purpose Synthetic Fluid
- Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Conditioned
- SABIC Innovative Plastics LNP THERMOCOMP DF004RXP PC (Asia Pacific)
- A. Schulman POLYAXIS® RLLP621 Flame Retardant, High Density Polyethylene
- Eagle Brass 220 Commercial Bronze, Spring
Copyright © lookpolymers.com All Rights Reserved