BASF Ultramid® B3S Q661 PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B3S Q661 PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid B3S Q661 is a general purpose, PA6 resin for injection molding.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Relative Viscosity	2.7 cP	2.7 cP	ISO Test; 96 % SAV
Viscosity Test	150 cm³/g	150 cm³/g	Viscosity number
Melt Flow	145 g/10 min @Load 5.00 kg, Temperature 275 °C	145 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	79.0 MPa	11500 psi	50mm/min; ISO 527
	79.0 MPa	11500 psi	2 in/min; ASTM Test
Elongation at Break	4.2 %	4.2 %	2 in/min; ASTM Test
Elongation at Yield	4.2 %	4.2 %	50mm/min; ISO 527
Tensile Modulus	1.107 GPa	160.6 ksi	1mm/min; ISO 527
Flexural Modulus	2.74 GPa	397 ksi	ASTM Test
Izod Impact, Notched	0.530 J/cm @Thickness 3.17 mm	0.993 ft-lb/in @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	215 °C	419 °F	ASTM Test
	220 °C	428 °F	10 K/min
Deflection Temperature at 0.46 MPa (66 psi)	180 °C	356 °F	ASTM Test
	180 °C	356 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	76.0 °C	169 °F	ASTM Test
	76.0 °C	169 °F	ISO 75

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding