SABIC Innovative Plastics LNP THERMOCOMP RFZ349XC PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RFZ349XC PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RFZ349XC is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% Milled Glass. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.430 % | 0.430 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0119 cm/cm @Time 86400 sec |
0.0119 in/in @Time 24.0 hour |
ISO 294 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| 124 MPa | 18000 psi | ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | ASTM D638 |
| 3.2 % | 3.2 % | ISO 527 | |
| Tensile Modulus | 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 |
| 11.4 GPa | 1650 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| 197 MPa | 28600 psi | ISO 178 | |
| Flexural Modulus | 7.17 GPa | 1040 ksi | ASTM D790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 237 °C @Thickness 3.20 mm |
459 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MS 20 U Linear Low Density Polyethylene
- Michelman® Michem® Lube 743 Nonionic paraffin wax emulsion
- STAR Thermoplastic Alloys & Rubbers StarMediflex P 7070-1000 TPE
- Samsung Cheil Industries Starex® SF-200H Expandable Polystyrene (EPS) FR
- Styron Modifier A/NA SB Latex
- Wellman Wellamid® MRGST1715-WBK1 Nylon 6, 25% Mineral and Glass Sphere Reinforced, Impact Modified, Weatherable Grade
- CMW® ELKONIUM 63 Silver Alloy
- Arlon R35640T003 0.003" (0.0762 mm) Uncured Silicone Rubber with Polyethylene Naphthalate Substrate
- Lubrizol ESTANE® 58206 Ester Based Thermoplastic Polyurethane (European Grade)
Copyright © lookpolymers.com All Rights Reserved