SABIC Innovative Plastics LNP THERMOCOMP RF007SXN PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF007SXN PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF007SXN is a Hydro-Stable, 35% Glass Fiber reinforced compound based on Nylon 66. Added features of this grade include: Heat Stabilized, NSF Listed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 3.79 g/cc | 3.79 g/cc | ASTM D792 |
| Density | 3.78 g/cc | 0.137 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.450 % | 0.450 % | 50% RH, 24 hrs; ASTM D570 |
| 0.510 % | 0.510 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | Type I, 5 mm/min; ASTM D638 |
| 193 MPa | 28000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 195 MPa | 28300 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.66 GPa | 1691 ksi | 1 mm/min; ISO 527 |
| 11.86 GPa | 1720 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 267 MPa | 38700 psi | ISO 178 |
| 284 MPa | 41200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 285 MPa | 41300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.83 GPa | 1430 ksi | 2 mm/min; ISO 178 |
| 10.6 GPa | 1540 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.0 J/cm | 18.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 61.0 kJ/m² | 29.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Fainplast Compounds RE 412/L Rigid PVC, Extrusion
- Lehmann & Voss LUVOCOM® 1105-7781/BK PEEK, with carbon fiber
- SABIC Innovative Plastics LNP LUBRICOMP RX88514 PA 66
- Teijin Multilon TN-7000F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
- A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Dow Corning LSPBK25 SILICONE MASTERBATCH BLACK
- ExxonMobil Bicor™ 52MBR666 OPP Film
- BASF LUMOGEN® 300 F Red
- Taiwan Sheen Soon Sheenthane® A9830 Thermoplastic Polyurethane Elastomer
- LATI Latamid 66 H2 G/25-V0KB4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved