SABIC Innovative Plastics LNP THERMOCOMP Noryl_PX5379 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP Noryl_PX5379 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* Noryl_PX5379 compound is a 10% GR. UL94 V-1 rated. Halogen free flame retardant. Typical applications are TV chassis, deflection yokes and connectors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.22 % | 0.22 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 104 | 104 | ASTM D785 |
| Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 119 MPa | 17300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.99 GPa | 579 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| 0.690 J/cm @Temperature -40.0 °C |
1.29 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C @Thickness 6.40 mm |
268 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 147 °C | 297 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.47 mm |
V-1 @Thickness 0.0579 in |
UL 94 |
| Oxygen Index | 31 % | 31 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dissipation Factor | 0.0016 @Frequency 1.00e+6 Hz |
0.0016 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0017 @Frequency 50.0 - 60.0 Hz |
0.0017 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 196 Gold Solder Alloy
- Indium Corp. Indalloy 213 Tin-Lead Solder Alloy
- Gwent Electronic Materials C2090225D7 Silver/Silver Chloride Paste
- SABIC Innovative Plastics ULTEM 1010TC PEI (Asia Pacific)
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- DuPont™ Surlyn® 9650 Ionomer Resin, Zinc
- ExxonMobil 20 Exxon XD-3
- Arlon LW202Txx-P1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- A.D. Compound Adene NTJA Homopolymer 30% Talc Filled Polypropylene
- Fainplast Compounds KL 92 Flexible PVC, Insulation for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved