Arlon R36601A010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R36601A010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Generation II Thermabond® NP electrically insulating electronic adhesive. Bonds without primer.Design/Construction: Liner 1: Polyethylene Side 1: Uncured Silicone Rubber Substrate: Style 1080 FiberglassSide 2: Uncured Silicone Rubber Liner 2: PolyethyleneThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.45 g/cc	0.0524 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	38.1 microns	1.50 mil	Liner 1
	38.1 microns	1.50 mil	Liner 2
	76.2 microns	3.00 mil	Substrate; Arlon SQA-TMS-003
	88.9 microns	3.50 mil	Side 1; Arlon SQA-TMS-003
	88.9 microns	3.50 mil	Side 2; Arlon SQA-TMS-003
	254 microns	10.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55	55	Silicone Property; ASTM D2240
Tensile Strength	5.86 MPa	850 psi	Silicone Property; ASTM D412
Elongation at Break	400 %	400 %	Silicone Property; ASTM D412
Modulus of Elasticity	0.00603 GPa	0.875 ksi	Silicone Property; ASTM E 831
Poissons Ratio	0.50	0.50	Approximately, Silicone Property
Shear Modulus	0.000331 GPa	0.0480 ksi	ASTM D 1002
Shear Strength	5.17 MPa	750 psi	Lap Shear Strength; ASTM D1002

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 µm/m-°C	22.2 µin/in-°F	Product Property; ASTM E 831
	180 µm/m-°C	100 µin/in-°F	Silicone Property; ASTM E 831
Specific Heat Capacity	1.00 J/g-°C	0.239 BTU/lb-°F	Product Property; E 1461-01
	1.14 J/g-°C	0.272 BTU/lb-°F	Silicone Property; E 1461-01
Thermal Conductivity	0.360 W/m-K	2.50 BTU-in/hr-ft²-°F	Product Property; ASTM E 1530
	0.400 W/m-K	2.78 BTU-in/hr-ft²-°F	Silicone Property; ASTM E 1530
Maximum Service Temperature, Air	204 °C	400 °F
Minimum Service Temperature, Air	-73.3 °C	-100 °F
Glass Transition Temp, Tg	<= -100 °C	<= -148 °F	Silicone Property; ASTM D3418
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.4 @Frequency 1.00e+6 Hz	3.4 @Frequency 1.00e+6 Hz	D<sub>k</sub>, Silicone Property; IPC TM 650 - 2.5.5.3
	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	D<sub>k</sub>, Product Property; IPC TM 650 - 2.5.5.3
Dielectric Strength	53.1 kV/mm	1350 kV/in	ASTM D149
Dissipation Factor	0.0050 @Frequency 1.00e+6 Hz	0.0050 @Frequency 1.00e+6 Hz	D<sub>f</sub>, Silicone Property; IPC TM 650 - 2.5.5.3
	0.0050 @Frequency 1.00e+6 Hz	0.0050 @Frequency 1.00e+6 Hz	D<sub>f</sub>, Product Property; IPC TM 650 - 2.5.5.3

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Pressure 0.0689 - 0.345 MPa, Temperature 121 °C	0.250 hour @Pressure 10.0 - 50.0 psi, Temperature 250 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 4.44 - 10.0 °C	6.00 Month @Temperature 40.0 - 50.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Light Blue
Total Product Weight (g/m2)	376	Arlon SQA-TMS-025