SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM3020 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM3020 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* Noryl_FM3020 compound is GR/MR 30%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
foam molded; ASTM D792
1.32 g/cc
1.32 g/cc
ASTM D792
Water Absorption 0.080 %

@Time 86400 sec
 0.080 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0025 cm/cm

@Thickness 6.40 mm
 0.0025 in/in

@Thickness 0.252 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0030 cm/cm

@Thickness 6.40 mm
 0.0030 in/in

@Thickness 0.252 in
 SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell M 83
83
ASTM D785
Tensile Strength, Yield 72.0 MPa

@Thickness 6.35 mm
 10400 psi

@Thickness 0.250 in
 ASTM D638
Elongation at Yield 2.0 %

@Thickness 6.35 mm
 2.0 %

@Thickness 0.250 in
 ASTM D638
Flexural Yield Strength 104 MPa
15100 psi
6.4 mm; ASTM D790
Flexural Modulus 6.55 GPa
950 ksi
6.4 mm; ASTM D790
Poissons Ratio 0.38
0.38
ASTM E 132
Izod Impact, Notched 0.960 J/cm

@Thickness 6.40 mm
 1.80 ft-lb/in

@Thickness 0.252 in
 ASTM D256
Coefficient of Friction, Static 0.51
0.51
steel; ASTM D1894
0.54
0.54
self; ASTM D1894
Taber Abrasion, mg/1000 Cycles 100
100
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
 13.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
CTE, linear, Transverse to Flow 34.2 µm/m-°C

@Temperature -40.0 - 95.0 °C
 19.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 118 °C

@Thickness 6.40 mm
 244 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C

@Thickness 6.40 mm
 230 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-1

@Thickness 2.89 mm
 V-1

@Thickness 0.114 in
 UL 94
5VA

@Thickness 2.89 mm
 5VA

@Thickness 0.114 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Surface Resistance 1.00e+17 ohm
1.00e+17 ohm
ASTM D257
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
UL 746A
Descriptive Properties Value Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction 20%
FOAM - Flame Class Minimum Density 1.12g/cm^3
FOAM - IMPACT 6.4 mm Wt Reduction 10%
FOAM - MECHANICAL 6.4 mm Wt Reduction 10%
FOAM - PHYSICAL 6.4mm Wt Reduction 10%
FOAM - THERMAL 6.4mm Wt Reduction 10%
Weight Reduction 10%
SABIC Method