SABIC Innovative Plastics Lexan® XHT4143T PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® XHT4143T PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.21 g/cc
0.0437 lb/in³
ISO 1183
Moisture Absorption 0.250 %
0.250 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.33 %
0.33 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0095 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0095 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 330 °C
25 g/10 min

@Load 4.76 lb,
Temperature 626 °F
ASTM D1238
Melt Index of Compound 24 g/10 min

@Load 2.16 kg,
Temperature 330 °C
24 g/10 min

@Load 4.76 lb,
Temperature 626 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 67.0 MPa
9720 psi
50 mm/min; ISO 527
69.0 MPa
10000 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 77.0 MPa
11200 psi
Type I, 50 mm/min; ASTM D638
78.0 MPa
11300 psi
50 mm/min; ISO 527
Elongation at Break 50 %
50 %
Type I, 50 mm/min; ASTM D638
50 %
50 %
50 mm/min; ISO 527
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
7.0 %
7.0 %
50 mm/min; ISO 527
Tensile Modulus 2.73 GPa
396 ksi
5 mm/min; ASTM D638
2.75 GPa
399 ksi
1 mm/min; ISO 527
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
120 MPa
17400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.60 GPa
377 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.930 J/cm
1.74 ft-lb/in
ASTM D256
0.760 J/cm

@Temperature -30.0 °C
1.42 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*3; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 72.0 J

@Temperature 23.0 °C
53.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 173 °C
343 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
174 °C

@Thickness 3.20 mm
345 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
165 °C

@Thickness 3.20 mm
329 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 181 °C
358 °F
Rate B/120; ISO 306
183 °C
361 °F
Rate B/50; ASTM D1525
183 °C
361 °F
Rate B/50; ISO 306
Glow Wire Test 850 °C

@Thickness 2.00 mm
1560 °F

@Thickness 0.0787 in
IEC 60695-2-12
960 °C

@Thickness 2.50 mm
1760 °F

@Thickness 0.0984 in
IEC 60695-2-12
Optical Properties Metric English Comments
Refractive Index 1.605
1.605
ASTM D542
Transmission, Visible 86 %
86 %
2.54 mm; ASTM D1003
Descriptive Properties Value Comments
Ball Pressure Test, 165°C +/- 2°C PASSES
IEC 60695-10-2