- Wellman Wellamid® MRGFX1716-BK1 40% Mineral/Glass Reinforced, Silicone Lubricated Nylon 6
Wellman Wellamid® MRGFX1716-BK1 40% Mineral/Glass Reinforced, Silicone Lubricated Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® MRGFX1716-BK1 40% Mineral/Glass Reinforced, Silicone Lubricated Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Mineral/Glass Reinforced, Silicone Lubricated Nylon 6Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183-87 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.010 cm/cm | 0.0090 - 0.010 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527-93 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-93 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178-93 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-93 |
Users viewing this material also viewed the following:
- Nilit Polynil® C50 PA66/6 Co-Polymer
- H.C. Starck Amperit® 716.054 Chromium Oxide-Titanium Oxide-Silicon Oxide 92-3-5 (Cr2O3-TiO2-SiO2)
- Chase Plastics CP Pryme® PC310GR Polycarbonate (Utility Grade), 10% Glass Fiber Reinforced, Mold Release
- A. Schulman POLYBATCH™ White 8350 AP Concentrate Based In LDPE
- Williams Advanced Alloys WS302 Solder
- ExxonMobil LLDPE LL 3402.48 Cast Linear Low Density Polyethylene Resin
- ExxonMobil Solvesso™ Aromatic 150 ND Aromatic Fluid
- Diamond Polymers NPP25-0620 Copolymer Polypropylene
- Fainplast Compounds HL 88 Flexible PVC, Insulation for High Temperatures
- BASF Ultramid® A3X2G5 25% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved