SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* M7001XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additves. Designed for touch surfaces in patient critical healthcare applications. Added features include: high antimicrobial performance, high mechanical strength, healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 32 g/10 min @Load 2.16 kg, Temperature 230 °C |
32 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
| 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.75 GPa | 254 ksi | 1 mm/min; ISO 527 |
| 1.80 GPa | 261 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
| Flexural Yield Strength | 40.0 MPa | 5800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.30 GPa | 189 ksi | 2 mm/min; ISO 178 |
| 1.45 GPa | 210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.250 J/cm | 0.468 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 105 °C @Thickness 3.20 mm |
221 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NanoAmor 60%, OD: 1-2 nm COOH Functionalized Single Walled Carbon Nanotubes
- Phillips 66 COPYLENE® CR750CL-02 Polypropylene, Random Copolymer, NX-8000 based
- Shandong Dongyue Shenzhou New Material Co 3-methoxy-2,2,3,3-tetrafluoropropionatemethylester (MTPME)
- SABIC Innovative Plastics LNP Stat-kon DX02731C PC
- A. Schulman FORMION™ FI 397 Ionomer
- DSM Biomedical BioSpan® S SPU Segmented Polyether Polyurethane (SPU)
- Fainplast Compounds FKT 0296/1 Flexible PVC, Insulation Lead Free
- Arkema Group Rilsan® AECV T8L Nylon 12, Cable Sheathing Grade (Conditioned)
- Carlisle 201HL Carbon-Carbon Composite
- BASF Styropor® BF 322 EPS
Copyright © lookpolymers.com All Rights Reserved