- SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66
SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon RX08408_NA1D004 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* RX08404_NA1D004 is a compound based on Nylon 66 containing Carbon Powder. Characteristics of this grade include: Electrically Conductive, High Impact.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Absorption at Equilibrium | 0.87 % | 0.87 % | 23°C / 50% RH; ISO 62 |
| 0.60 % @Time 86400 sec |
0.60 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.030 - 0.050 cm/cm @Time 86400 sec |
0.030 - 0.050 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.030 - 0.050 cm/cm @Time 86400 sec |
0.030 - 0.050 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D 638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 26 % | 26 % | Type I, 5 mm/min; ASTM D 638 |
| 26 % | 26 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.93 GPa | 280 ksi | 1 mm/min; ISO 527 |
| 1.96 GPa | 284 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 61.0 MPa | 8850 psi | ISO 178 |
| Flexural Modulus | 1.76 GPa | 255 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 1.85 GPa | 268 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.41 J/cm @Temperature 23.0 °C |
2.64 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 17.2 J/cm @Temperature 23.0 °C |
32.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 196 kJ/m² @Temperature 23.0 °C |
93.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 25.0 J | 18.4 ft-lb | Multiaxial Impact; ISO 6603 |
| 22.0 J @Temperature 23.0 °C |
16.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature -30.0 - 30.0 °C |
61.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 114 µm/m-°C @Temperature -30.0 - 30.0 °C |
63.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D 257 |
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Overview of materials for Phenolic/Rubber; Molded
- Huntsman IROGRAN® A 95 E 4813 Polyester-Based TPU-High Performance Grade
- Huntsman AVALON® 65 ABX Thermoplastic Polyurethane
- A. Schulman POLYFORT™ PP 7001
- China Tungsten ST1265 PM Antifriction Parts
- EPICHEM Epilon PC UVR Polycarbonate, High Impact
- Ascend Performance Materials Vydyne® R533T Nylon 66, Translucent, 33% Glass Filled, Conditioned (2.5% Moisture)
- Beijing Evergrow Resources ER-WR-20G Polypropylene Super-Fine Filter Material
Copyright © lookpolymers.com All Rights Reserved