A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 2.20 J/cm | 4.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
| UL RTI, Electrical | 105 °C | 221 °F | 0.030 in; UL 94 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Network Polymers Softflex® 7200
- SABIC Innovative Plastics Lexan® EXL1434T PC Copolymer
- Eastman Aqua WA314 PET (discontinued **)
- High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, After Process Annealed at 1600°F (871°C)
- SABIC Innovative Plastics LNP Lubricomp UL004AS PPA (Europe-Africa-Middle East)
- Samsung Cheil Industries Infino® HP-1000H PC/ABS, Unreinforced
- Styron CALIBREâ„¢ 201-15 Polycarbonate Resin
- ExxonMobil Oppalyte™ 60MH247 OPP Film
- Beijing Evergrow Resources ACFC1500 Activated Carbon Fiber Cloth
- LNP Thermocomp® UF-1008 Polyphthalamide, Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved