- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Chi Mei Polylac® PA-765B ABS - Flame Retardant
Chi Mei Polylac® PA-765B ABS - Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-765B ABS - Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
F.R. Medium Impact
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 4.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 42 g/10 min @Load 10.0 kg, Temperature 220 °C |
42 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Ball Indentation Hardness | 82.0 MPa | 11900 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 2.22 J/cm @Thickness 6.35 mm |
4.16 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.66 J/cm @Thickness 3.17 mm |
4.98 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 |
| Impact | 13.0 | 13.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | unannealed; ISO 75 |
| 91.0 °C | 196 °F | annealed; ISO 75 | |
| Vicat Softening Point | 79.0 °C @Load 5.00 kg |
174 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 82.0 °C @Load 5.00 kg |
180 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 90.0 °C @Load 1.00 kg |
194 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 92.0 °C @Load 1.00 kg |
198 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | V-2 @Thickness 2.12 mm |
V-2 @Thickness 0.0833 in |
UL 94 |
| V-0 @Thickness 2.54 mm |
V-0 @Thickness 0.100 in |
UL 94 | |
| 5VA @Thickness 3.17 mm |
5VA @Thickness 0.125 in |
UL 94 |
Users viewing this material also viewed the following:
- MarkeTech AO 95 Aluminum Oxide Ceramic Substrate, 95% Purity
- DSM Biomedical PurSil® 35 Thermoplastic Silicone Polyether Polyurethane (TSPU)
- DSM Arnite® B427 SE/R PBT-GF35 FR(17)
- ExxonMobil Bicor® 70 HSH OPP Film
- CP-Polymer-Technik Wellamid® 6000 MZ 301 CP Combination Nylon 6, Heat Stabilized, Dry
- Eurostar Staramide ACF4 PA66, 20% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
- 3M AC-251 Black Class B-2 Aerospace Sealant
- Asahi Kasei Leona® 1402 Polyamide 66 Resin
- 3M 7014FL Performance Paper Label Material
- DuPont Performance Polymers Delrin® 300CP BK642 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved