PTS Trimid® N66-G13 13% Glass Fiber Reinforced Nylon 6/6

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name Trimid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS Trimid® N66-G13 13% Glass Fiber Reinforced Nylon 6/6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 100 MPa
14500 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Modulus 4.65 GPa
674 ksi
ASTM D790
Izod Impact, Notched 0.430 J/cm

@Thickness 3.17 mm
 0.806 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 254 °C
489 °F
ASTM D789
Deflection Temperature at 1.8 MPa (264 psi) 232 °C
450 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 254 °C
490 °F
Middle Barrel Temperature 268 °C
515 °F
Front Barrel Temperature 285 °C
545 °F
Nozzle Temperature 266 - 282 °C
510 - 540 °F
Melt Temperature 271 - 293 °C
520 - 560 °F
Mold Temperature 26.7 - 93.3 °C
80.0 - 200 °F
Drying Temperature 71.1 °C
160 °F
Dry Time 4 hour
4 hour
Injection Pressure 68.9 MPa
10000 psi
Back Pressure 0.0689 - 0.689 MPa
10.0 - 100 psi
Screw Speed 30 - 60 rpm
30 - 60 rpm