SABIC Innovative Plastics LNP Lubricomp QP003 PA 6/10 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp QP003 PA 6/10 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* QP003 is a compound based on Nylon 6/10 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
1.17 g/cc
0.0423 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.30 %

@Time 86400 sec
 0.30 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.019 - 0.021 cm/cm

@Time 86400 sec
 0.019 - 0.021 in/in

@Time 24.0 hour
 ASTM D 955
0.020 cm/cm

@Time 86400 sec
 0.020 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.021 - 0.023 cm/cm

@Time 86400 sec
 0.021 - 0.023 in/in

@Time 24.0 hour
 ASTM D 955
0.022 cm/cm

@Time 86400 sec
 0.022 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
ASTM D 638
51.0 MPa
7400 psi
ISO 527
Tensile Strength, Yield 48.0 MPa
6960 psi
ASTM D 638
51.0 MPa
7400 psi
ISO 527
Elongation at Break 11.9 %
11.9 %
ASTM D 638
14 %
14 %
ISO 527
Elongation at Yield 13.8 %
13.8 %
ISO 527
16.5 %
16.5 %
ASTM D 638
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D 638
2.29 GPa
332 ksi
1 mm/min; ISO 527
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Modulus 1.37 GPa
199 ksi
ASTM D 790
2.00 GPa
290 ksi
ISO 178
Izod Impact, Notched 0.420 J/cm

@Temperature 23.0 °C
 0.787 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 8.33 J/cm

@Temperature 23.0 °C
 15.6 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²

@Temperature 23.0 °C
 21.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 15.0 J
11.1 ft-lb
Multiaxial Impact; ISO 6603
3.00 J

@Temperature 23.0 °C
 2.21 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.19
0.19
ASTM D 3702 Modified
Coefficient of Friction, Static 0.15
0.15
ASTM D 3702 Modified
K (wear) Factor 6.04 x 10-8 mm³/N-M
3.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 98.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 54.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
99.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 55.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 97.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 53.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
97.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 54.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
163 °C

@Thickness 3.20 mm
 325 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 58.0 °C
136 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
57.0 °C

@Thickness 3.20 mm
 135 °F

@Thickness 0.126 in
 unannealed; ASTM D 648