Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer Solvay Specialty Polymers
Trade Name KetaSpire®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers KetaSpire® KT-820 SL10 Polyetheretherketone (PEEK).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KetaSpire® KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear resistance, this grade offers high lubricity while retaining outstanding ductility and toughness that surpasses that of unmodified high viscosity PEEK. Also, this product offers high melt flow, which allows injection molding of thin, intricate, or complex parts.In addition to these differentiating features, this resin also offers the outstanding combination of ultra-performance attributes commonly known for PEEK. These include: mechanical strength and stiffness even at elevated temperatures, long term thermal-oxidative stability, fatigue resistance, and excellent chemical resistance to a broad range of harsh chemical environments including acids, bases, and organics.The attractive combination of properties make KetaSpire® KT-820 SL10 suitable for applications in transportation, electronics, chemical processing, and industrial uses including oil and gas exploration and production.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Wear Resistance; High Heat ResistanceUses: Film; Industrial Applications; Oil/Gas Applications; Profiles; Rods; Sheet; TubingInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ISO 62
Viscosity 170000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
170000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.012 - 0.014 cm/cm

@Thickness 3.18 mm
0.012 - 0.014 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.016 - 0.018 cm/cm

@Thickness 3.18 mm
0.016 - 0.018 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore D 83
83
1 sec; ASTM D2240
Tensile Strength 88.0 MPa
12800 psi
50 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type 1A, 50 mm/min; ISO 527-2
60 %
60 %
50 mm/min; ASTM D638
Elongation at Yield 5.2 %
5.2 %
50 mm/min; ASTM D638
Tensile Modulus 3.60 GPa
522 ksi
50 mm/min; ASTM D638
Flexural Strength 134 MPa
19400 psi
ASTM D790
Flexural Yield Strength 134 MPa
19400 psi
ASTM D790
Flexural Modulus 3.50 GPa
508 ksi
ASTM D790
Izod Impact, Notched 1.70 J/cm
3.18 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Annealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 365 °C
689 °F
Middle Barrel Temperature 370 °C
698 °F
Front Barrel Temperature 375 °C
707 °F
Nozzle Temperature 380 °C
716 °F
Mold Temperature 175 - 205 °C
347 - 401 °F
Drying Temperature 150 °C

@Time 14400 sec
302 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Injection Rate Fast
Processing Technique Injection Molding; Machining; Profile Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.5:1.0 to 3.5:1.0