Chosun Refractories INCT-135N Light-Weight Castable
| Category | Ceramic |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT-135N Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 3.37e-7 - 0.00147 GPa @Temperature 110 °C, Time 86400 sec |
0.0000489 - 0.213 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0004905 - 0.0024525 GPa @Temperature 1000 °C, Time 10800 sec |
0.07114 - 0.35571 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.0014715 - 0.0034335 GPa @Temperature 500 °C, Time 10800 sec |
0.21343 - 0.49799 ksi @Temperature 932 °F, Time 3.00 hour |
||
| Compressive Strength | 4.90 - 9.81 MPa @Temperature 110 °C, Time 86400 sec |
711 - 1420 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 4.90 - 9.81 MPa @Temperature 500 °C, Time 10800 sec |
711 - 1420 psi @Temperature 932 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 4.90 - 9.81 MPa @Temperature 1000 °C, Time 10800 sec |
711 - 1420 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.3955 W/m-K @Temperature 260 °C |
2.740 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.44200 W/m-K @Temperature 540 °C |
3.0625 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.48852 W/m-K @Temperature 800 °C |
3.3849 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1350 °C | 2460 °F | limited |
| Shrinkage | -0.450 % @Temperature 1000 °C, Time 10800 sec |
-0.450 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 38 % | 38 % | |
| SiO2 | 48 % | 48 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | High temperature Low thermal conductivity | |
| Material Required for Estimating (kg/?) | 1,250 | |
| Water Required for Casting(%) | 30-40 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP WCL36 PBT
- SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP
- ELASTO UK Dryflex® 8004-101 Flame Retardant TPE for Injection Molding, Black, Halogen Free
- DuPont™ Surlyn® 9120 Ionomer Resin, Zinc
- China Tungsten YG12X Tungsten Carbide
- DuPont Teijin Films Melinex® 453 Polyester Film, 92 Gauge
- Carmel Olefins CAPILENE® T 12 EV Polypropylene Homopolymer
- DuPont™ Clysar® EZ Polyolefin Shrink Packaging Film, 50 Gauge (discontinued **)
Copyright © lookpolymers.com All Rights Reserved