SABIC Innovative Plastics LNP Lubricomp KI001A Acetal

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Silicone Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp KI001A Acetal.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp Fulton 441D is an Acetal based compound with Silicone.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ASTM D 792
1.40 g/cc
0.0506 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.47 %
0.47 %
23°C / 50% RH; ISO 62
0.33 %

@Time 86400 sec
 0.33 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
5 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 60.0 MPa
8700 psi
5 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 24.8 %
24.8 %
5 mm/min; ISO 527
32 %
32 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 22.3 %
22.3 %
Type I, 5 mm/min; ASTM D 638
24.8 %
24.8 %
5 mm/min; ISO 527
Tensile Modulus 2.98 GPa
432 ksi
1 mm/min; ISO 527
3.21 GPa
466 ksi
50 mm/min; ASTM D 638
Flexural Strength 69.0 MPa
10000 psi
ISO 178
Flexural Modulus 2.63 GPa
381 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.68 GPa
389 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.710 J/cm

@Temperature 23.0 °C
 1.33 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 15.1 J/cm

@Temperature 23.0 °C
 28.3 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 83.0 kJ/m²

@Temperature 23.0 °C
 39.5 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.41
0.41
ASTM D 3702 Modified
Coefficient of Friction, Static 0.30
0.30
ASTM D 3702 Modified
K (wear) Factor 220 x 10-8 mm³/N-M
109 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 97.8 µm/m-°C

@Temperature -30.0 - 30.0 °C
 54.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 96.9 µm/m-°C

@Temperature -30.0 - 30.0 °C
 53.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 157 °C
315 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
99.0 °C

@Thickness 3.20 mm
 210 °F

@Thickness 0.126 in
 unannealed; ASTM D 648