LATI Latimass 62-05 D040 PA6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	LATI
Trade Name	Latimass
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latimass 62-05 D040 PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Specific density compound based on Polyamide 6 (PA6). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	4.50 g/cc	0.163 lb/in³
Linear Mold Shrinkage, Flow	0.0035 - 0.0065 cm/cm	0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse	0.0030 - 0.0060 cm/cm	0.0030 - 0.0060 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	40.0 MPa	5800 psi
Elongation at Break	0.40 %	0.40 %
Tensile Modulus	13.0 GPa	1890 ksi
Charpy Impact Unnotched	0.800 J/cm²	3.81 ft-lb/in²
Charpy Impact, Notched	0.250 J/cm²	1.19 ft-lb/in²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	185 °C	365 °F
Deflection Temperature at 1.8 MPa (264 psi)	170 °C	338 °F
Vicat Softening Point	200 °C @Load 5.00 kg	392 °F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	240 - 280 °C	464 - 536 °F
Mold Temperature	80.0 - 100 °C	176 - 212 °F
Drying Temperature	90.0 - 100 °C @Time 10800 sec	194 - 212 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa