SABIC Innovative Plastics LNP LUBRICOMP Noryl_SPN422L PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP Noryl_SPN422L PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* Noryl_SPN422L compound is a wear resistant, fluorocarbon alloy, 235F (113C) HDT. UL94 HB rated. Check surface aesthetics prior to material specification.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.27 GPa | 329 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| 0.960 J/cm @Temperature -40.0 °C |
1.80 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Gardner Impact | 13.0 J | 9.59 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C @Thickness 6.40 mm |
234 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- DuPont Elvax® 4320 Ethylene Vinyl Acetate (discontinued **)
- Lehmann & Voss LUVOCOM® 6-8438-1 Polyamide 12, with glass fiber
- Styrolution PS 168N GPPS
- SABIC Innovative Plastics LNP STAT-KON REF42 PA 66
- Silberline Sparkle Silvet® 760-20-E
- Beijing Evergrow Resources UHF-W800 UHMW PE Fiber
- Aaron Industries AAROLENE® ARPP H 200-1 PP Black Polypropylene Homopolymer Compounded Resin
- Techmer ES HiFill® PA6/6 GFB20 20% Glass/Glass Bead Filled
Copyright © lookpolymers.com All Rights Reserved