- Thermoplastic
- Acetal (POM)
- Acetal Copolymer, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer
SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KFL36 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 g/cc | 1.75 g/cc | ASTM D792 |
| Density | 1.75 g/cc | 0.0632 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 |
| 1.3 % | 1.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.61 GPa | 1539 ksi | 1 mm/min; ISO 527 |
| 10.82 GPa | 1569 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 107 MPa | 15500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 130 MPa | 18900 psi | ISO 178 | |
| Flexural Modulus | 9.28 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.93 GPa | 1440 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.46 | 0.46 | ASTM D3702 Modified |
| K (wear) Factor | 471 x 10-8 mm³/N-M | 234 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
52.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 64.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 183 °C @Thickness 3.20 mm |
361 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Chevron Phillips HiD® 99413F with Food Grade Antistat HDPE Blow Molding Resin (discontinued **)
- Sylvin Technologies 9999-95 Natural PVC Molding Compound
- SGL Carbon Group SIGRAFIL C® C10 S003 GLY Staple Carbon Fiber, Glycerine Sizing
- Unifrax Fiberfrax® LDS AL-Moldable Moldable Insulation
- Eagle Brass 18665 MSP1, Extra Hard
- ExxonMobil ESCOREZ™ 5340 Petroleum Hydrocarbon Resin
- DuPont Performance Polymers Zytel® HTN 51G35NOX BK420 Polyphthalamide (PPA)
- Fainplast Compounds HAX HFX 024-21L Halogen Free PVC
- Abatron Abokote 8106-1 Water-Based Epoxy Coating for Floors
Copyright © lookpolymers.com All Rights Reserved