SABIC Innovative Plastics LNP LUBRICOMP DL002 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DL002 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DL002 is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 53 % | 53 % | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 2.27 GPa | 329 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.28 | 0.28 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.17 | 0.17 | ASTM D3702 Modified |
| K (wear) Factor | 195 x 10-8 mm³/N-M | 97.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP GRMF30 Homopolymer Polypropylene Glass/Mineral Filled
- LG Chemical SEETEC BS500 LDPE
- LyondellBasell Hostacomâ„¢ BG749GC/1 Polypropylene Copolymer
- SABIC Innovative Plastics Valox® 430 PBT (Asia Pacific)
- A. Schulman POLYBATCH™ White 8350/UV5 Concentrate Based In Polyethylene
- Master Bond UV15TK High Temperature Resistant One Component UV Curable System
- Elektro-Isola Etronit IV C Phenolic, Paper Reinforcement, Yellow, Tubes
- DuPont Teijin Films Melinex® 329 Polyester Film, 380 Gauge
- Clariant Renol PA111G60 Nylon 66, 60% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved