Akro-Plastic Akromid® B3 GF 50 9 RM-M (3147) PA 6 Dry, 50% Glass Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Akro-Plastic
Trade Name Akromid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akromid® B3 GF 50 9 RM-M (3147) PA 6 Dry, 50% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
In all, the construction relevant features show that the significantly reduced moisture absorption of AKROMID B3 GF 30 RM leads to increasing rigidities and strengths as already expected. Nevertheless, the viscosity features are on the level of PA6. Especially after storage, e.g. at 150° AKROMID RM shows comparable ageing characteristics. For appliances with very constant features, low warpage, very good finish together with an improved chemical resistance and for production of parts according to the GIT/WIT process, the version B3 GF 30 RM 9 black (3099) or respectively B3 GF 50 9 RM black (3147) offers an ideal solution. However, if a very good impact strength is predominant, our type B3 GF 30 RM black (3016) or respectively B3 GF 50 RM black (3146) will be favored.High quality surface finish:B3 GF 30 9 RM black (3099)/B3 GF 50 9 RM black (3147)Very constant features with regard to climateVery low warpageVery good surfaceCaCI2 resistantCost-effective:B3 GF 30 RM black (3016)/B3 GF 50 RM black (3146)Closer to PA 6 GF 30/GF 50Constant features with regard to climateLow warpageTendentious higher impact strengthTendentious higher notched impactApplications:Electronic market:e.g. sensor housings, coil former (wo.UL), plug-in connectors, plug panels etc.Automobile market:e.g. sensor housing, electrical parts, wind screen wiper bows, door handles, mirror elements, sliding roof frames etc.General mechanical engineering:e.g. control elements in printer, copier, housings of valves, pumps etc.Information from Akro-Plastic
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ISO 1183
Filler Content 50 %
50 %
ISO 1172
Water Absorption 1.2 %

@Temperature 70.0 °C
1.2 %

@Temperature 158 °F
62% RH, Humidity; ISO 1110
Moisture Absorption 0.450 %

@Temperature 70.0 °C,
Time 180000 sec
0.450 %

@Temperature 158 °F,
Time 50.0 hour
62% RH
0.700 %

@Temperature 70.0 °C,
Time 720000 sec
0.700 %

@Temperature 158 °F,
Time 200 hour
62% RH
1.00 %

@Temperature 70.0 °C,
Time 1.44e+6 sec
1.00 %

@Temperature 158 °F,
Time 400 hour
62% RH
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4
Spiral Flow 50.0 cm
19.7 in
7 x 4 [mm] diameter
Mechanical Properties Metric English Comments
Ball Indentation Hardness 280 MPa
40600 psi
H 961/30; ISO 2039-1
Tensile Strength at Break 210 MPa
30500 psi
5 [mm/min]; ISO 527-2/5
Tensile Strength 160 MPa

@Temperature 70.0 °C,
Time 1.44e+6 sec
23200 psi

@Temperature 158 °F,
Time 400 hour
62% RH
175 MPa

@Temperature 70.0 °C,
Time 720000 sec
25400 psi

@Temperature 158 °F,
Time 200 hour
62% RH
180 MPa

@Temperature 70.0 °C,
Time 180000 sec
26100 psi

@Temperature 158 °F,
Time 50.0 hour
62% RH
Elongation at Break 2.2 %
2.2 %
5 [mm/min]; ISO 527-2/5
Tensile Modulus 16.0 GPa
2320 ksi
1 [mm/min]; ISO 527-2/1
13.5 GPa

@Temperature 70.0 °C,
Time 1.44e+6 sec
1960 ksi

@Temperature 158 °F,
Time 400 hour
62% RH
14.0 GPa

@Temperature 70.0 °C,
Time 720000 sec
2030 ksi

@Temperature 158 °F,
Time 200 hour
62% RH
15.0 GPa

@Temperature 70.0 °C,
Time 180000 sec
2180 ksi

@Temperature 158 °F,
Time 50.0 hour
62% RH
Charpy Impact Unnotched 6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
7.00 J/cm²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
DIN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Unannealed; ISO 75-2/A
Deflection Temperature at 8.0 MPa 165 °C
329 °F
Unannealed; ISO 75-2/C
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Nozzle Temperature 240 - 280 °C
464 - 536 °F
Zone 1 225 - 300 °C
437 - 572 °F
Zone 2 225 - 300 °C
437 - 572 °F
Zone 3 225 - 300 °C
437 - 572 °F
Zone 4 225 - 300 °C
437 - 572 °F
Melt Temperature 260 - 300 °C
500 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 - 12.0 hour
4.00 - 12.0 hour
Hold Pressure 75.0 MPa
10900 psi
Back Pressure 5.00 - 10.0 MPa
725 - 1450 psi
Descriptive Properties Value Comments
Acetone Pass
100% Conc
Benzine Pass
100% Conc
Benzol Pass
100% Conc
Biodiesel Pass
50°C, 100% Conc
Brake Fluid (DOT4) Fail
130°C, 100% Conc
Pass
100% Conc
Calcium chloride, alcoholic Fail
10% Conc
Pass
10% Conc, when surface treated with 4 (chemical-stabilized)
Calcium chloride, aqueous Fail
10% Conc
Pass
10% Conc, when surface treated with 4 (chemical-stabilized)
Citric acid Pass
10% Conc
Diesel fuel (DIN 51601) Pass
100% Conc
Sulphuric acid Fail
96% Conc
Toluene Pass
100% Conc
Water Pass
100% Conc
Zinc chloride, aqueous Fail
50% Conc