- A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm @Thickness 3.175 mm |
0.0060 in/in @Thickness 0.1250 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17200 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 5.79 GPa | 840 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.48 J/cm | 8.40 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
| Moisture Content | 0.080 - 0.12 % | 0.080 - 0.12 % |
Users viewing this material also viewed the following:
- Cos70 Cork/Synthetic Rubber Sheet
- Lehmann & Voss LUVOCOM® 1/XCF/30 Polyamide 66, with carbon fiber, heat stabilized
- Heraeus Cleviosâ„¢ P Jet HC Conductive Sulfonate Polymer for Antistatic Coatings
- Solvay TECHNYLSTARâ„¢ SX 216 V50 PA6, 50% glass filled, Conditioned
- Solvay Specialty Polymers Cogegum® AFR/920-UV Polyolefin
- Teknor Apex Chemlon® 133 GVH Nylon 66, 30% Glass Fiber Reinforced
- ExxonMobil Exxtral™ LNT 010 Performance Polyolefin
- DuPont Performance Polymers Crastin® SK601 BK851 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Ashley Polymers Ashlene® P258 PPO
Copyright © lookpolymers.com All Rights Reserved