SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Carbon Fiber Reinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
1.56 g/cc
0.0564 lb/in³
ASTM D792
Moisture Absorption 0.300 %
0.300 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0070 cm/cm

@Time 86400 sec
 0.0070 in/in

@Time 24.0 hour
 ASTM D955
0.0073 cm/cm

@Time 86400 sec
 0.0073 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.013 cm/cm

@Time 86400 sec
 0.013 in/in

@Time 24.0 hour
 ASTM D955
0.013 cm/cm

@Time 86400 sec
 0.013 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 87.0 MPa
12600 psi
ASTM D638
88.0 MPa
12800 psi
ISO 527
Tensile Strength, Yield 87.0 MPa
12600 psi
ASTM D638
88.0 MPa
12800 psi
ISO 527
Elongation at Break 0.70 %
0.70 %
ASTM D638
0.70 %
0.70 %
ISO 527
Elongation at Yield 0.70 %
0.70 %
ASTM D638
0.70 %
0.70 %
ISO 527
Tensile Modulus 15.51 GPa
2250 ksi
1 mm/min; ISO 527
17.23 GPa
2499 ksi
50 mm/min; ASTM D638
Flexural Strength 110 MPa
16000 psi
ASTM D790
117 MPa
17000 psi
ISO 178
Flexural Modulus 13.1 GPa
1900 ksi
ASTM D790
15.0 GPa
2180 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.67 J/cm
5.00 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J
2.95 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.35
0.35
ASTM D3702 Modified
Coefficient of Friction, Static 0.32
0.32
ASTM D3702 Modified
K (wear) Factor 139 x 10-8 mm³/N-M
69.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 36.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
175 °C

@Thickness 3.20 mm
 347 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
171 °C

@Thickness 3.20 mm
 340 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 6.0 ohm
6.0 ohm
ASTM D257