LG Chemical LUPOL HI5302S PP+MF15%, High Impact
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL HI5302S PP+MF15%, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP+MF15%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsInformation provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.011 - 0.013 cm/cm @Thickness 3.20 mm |
0.011 - 0.013 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.5 MPa @Thickness 3.20 mm |
3700 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 80 % @Thickness 3.20 mm |
80 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 43.1 MPa @Thickness 6.40 mm |
6260 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa @Thickness 6.40 mm |
370 ksi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Izod Impact, Notched | >= 1.47 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 2.76 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ LSR 2742 Liquid Silicone Rubber - Self-Bonding
- Momentive Performance Materials Siloprenâ„¢ LSR 3786/20 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- Teknor Apex Telcar® OBC 4530A Thermoplastic Elastomer
- A. Schulman POLYFORT™ PP 3701
- Bohler-Uddeholm ORVAR® 2M / AISI H13 Hot Work Tool Steel
- 3M Cushion-Mount™ E1040H Plus Plate Mounting Tapes with Easy Mount Adhesive and High Plateside Adhesion
- Karina 802-10/55-AY-ERYB White PVC Compound
- CEN® Electronic Material CN Polyimide Film, 6 Mil Thickness
Copyright © lookpolymers.com All Rights Reserved