SABIC Innovative Plastics GELOY XP4025 ASA+PC

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY XP4025 ASA+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Available in a wide range of colors and is recommended for unpainted exterior applications.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Water Absorption 0.24 %

@Time 86400 sec
 0.24 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 6.7 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.7 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
18 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 18 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
31 g/10 min

@Load 3.80 kg,
Temperature 280 °C
 31 g/10 min

@Load 8.38 lb,
Temperature 536 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength at Break 44.0 MPa
6380 psi
50 mm/min; ISO 527
Tensile Strength, Yield 58.0 MPa
8410 psi
50 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 25 %
25 %
Type I, 50 mm/min; ASTM D638
64 %
64 %
50 mm/min; ISO 527
Elongation at Yield 4.1 %
4.1 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
Flexural Yield Strength 75.0 MPa
10900 psi
2 mm/min; ISO 178
88.0 MPa
12800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.58 GPa
374 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.70 J/cm
3.18 ft-lb/in
ASTM D256
0.640 J/cm

@Temperature -30.0 °C
 1.20 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 21.0 kJ/m²
9.99 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 3.70 J/cm²
17.6 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 33.0 J

@Temperature -30.0 °C
 24.3 ft-lb

@Temperature -22.0 °F
 ASTM D3763
39.0 J

@Temperature 23.0 °C
 28.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -20.0 - 150 °C
 40.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -20.0 - 150 °C
 40.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 107 °C
225 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
102 °C

@Thickness 3.20 mm
 216 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
90.0 °C

@Thickness 6.40 mm
 194 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 109 °C
228 °F
Rate B/50; ISO 306
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.47 mm
 HB

@Thickness 0.0579 in
 UL 94
Optical Properties Metric English Comments
Gloss 90 %
90 %
untextured, 60 degrees; ASTM D523