SABIC Innovative Plastics GELOY CR7020 ASA

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY CR7020 ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ASA copolymer. Profile/sheet coextrusion over ABS. Excellent weatherability, good flow/aesthetics and high impact.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Moisture Absorption at Equilibrium 0.55 %
0.55 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
13 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 13 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 86
86
ASTM D785
Tensile Strength at Break 34.0 MPa
4930 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 41.0 MPa
5950 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 40 %
40 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.79 GPa
260 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 58.0 MPa
8410 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.79 GPa
260 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.20 J/cm
5.99 ft-lb/in
ASTM D256
0.580 J/cm

@Temperature -30.0 °C
 1.09 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Dart Drop, Total Energy 25.0 J

@Temperature 23.0 °C
 18.4 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact 10675
10675
J/m Gardner; ASTM D4226
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.6 µm/m-°C

@Temperature -30.0 - 0.000 °C
 47.0 µin/in-°F

@Temperature -22.0 - 32.0 °F
 ASTM E 831
86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
90.0 µm/m-°C

@Temperature 0.000 - 100 °C
 50.0 µin/in-°F

@Temperature 32.0 - 212 °F
 ASTM E 831
CTE, linear, Transverse to Flow 91.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 unannealed; ASTM D648
90.0 °C

@Thickness 6.40 mm
 194 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
annealed; ASTM D648
76.0 °C

@Thickness 3.20 mm
 169 °F

@Thickness 0.126 in
 unannealed; ASTM D648
79.0 °C

@Thickness 6.40 mm
 174 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 99.0 °C
210 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.49 mm
 HB

@Thickness 0.0587 in
 UL 94
Optical Properties Metric English Comments
Gloss 95 %
95 %
untextured, 60 degrees; ASTM D523
Electrical Properties Metric English Comments
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Dielectric Constant 3.21

@Frequency 1.00e+6 Hz
 3.21

@Frequency 1.00e+6 Hz
 ASTM D150
5.2

@Frequency 50.0 - 60.0 Hz
 5.2

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Dielectric Strength 15.9 kV/mm

@Thickness 3.20 mm
 404 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
Dissipation Factor 0.026

@Frequency 1.00e+6 Hz
 0.026

@Frequency 1.00e+6 Hz
 ASTM D150
0.15

@Frequency 50.0 - 60.0 Hz
 0.15

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Comparative Tracking Index >= 600 V
>= 600 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
UV-light, water exposure/immersion F2
UL 746C