| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® X37 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS, injection moulding, high heat grade.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D 785 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.530 J/cm @Temperature -40.0 °C |
0.993 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 2.13 J/cm @Temperature 23.0 °C |
3.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Gardner Impact | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C @Thickness 6.40 mm |
217 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 94 % | 94 % | untextured, 60 degrees; ASTM D 523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 36.8 kV/mm @Thickness 1.60 mm |
935 kV/in @Thickness 0.0630 in |
in air; ASTM D 149 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten, PLC code 6; ASTM D 495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC code 0; UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | PLC code 3; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min | PLC code 1; UL 746A |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA - 51 LL General Purpose Acrylic Resin
- LNP ULTEM® SMU6303 Polyetherimide, 5% Glass Fiber Reinforcement, 5% PTFE Lubricant (discontinued **)
- LATI Larpeek 10 K/20 PEEK, 20% Carbon Fiber Reinforced
- Tisan TISAPET® 30% Glass Reinforced Polyethylene Terephthalate
- A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
- Asahi Glass Fluon® CD123 PTFE Coagulated Dispersion Powder
- 3M Scotch-Weld™ 6111HT Tan Bulk only Adhesive
- Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes
- SABIC Innovative Plastics Valox® VX4930 PBT (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved