Oxford Polymers 20GF 20% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 20% Glass Fiber |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers 20GF 20% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass Fiber Filled Polyetherimide for Extrusion and Injection MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Water Absorption | 0.19 % | 0.19 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 132 MPa | 19100 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Tensile Modulus | 6.72 GPa | 975 ksi | ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 5.69 GPa | 825 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Temperature 23.0 °C |
1.40 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 382 °C | 720 °F |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9730 TPE, ABS/PC Overmold
- SABIC PVC 70S Suspension Polyvinyl Chloride for Flexible Products
- NBE nanoTach® Nano-Silver Paste, Lead-Free Solder Alternative
- Westlake EMAC® SP1400 Specialty Copolymer (discontinued **)
- NIZHNEKAMSKNEFTEKHIM PE 4436S (35405) Medium Density Polyethylene
- H.C. Starck Amperit® 740.3 Aluminum Oxide (Al2O3)
- Kuraray SEPTON® A4 Hot Melt Adhesive
- Plenco 00732 Melamine-Phenolic, Granular, Compression Molded
- BASF Neopolen® P 9270 0.08 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved