Techmer ES HiFillÂ® PES GF20 TL15 LE 20% Glass Filled

Category	Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled , Polyethersulfone (PES), PTFE Filled
Manufacturer	Techmer ES
Trade Name	HiFill®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES HiFillÂ® PES GF20 TL15 LE 20% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightPTFE LubricantFeatures: Low Extractables and LubricatedInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.62 g/cc	0.0585 lb/inÂ³	ASTM D792
Water Absorption	0.18 % @Time 86400 sec	0.18 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0010 cm/cm @Thickness 3.17 mm	0.0010 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength, Yield	124 MPa	18000 psi	ASTM D638
Elongation at Break	2.0 %	2.0 %	ASTM D638
Flexural Strength	167 MPa	24200 psi	ASTM D790
Flexural Modulus	6.55 GPa	950 ksi	ASTM D790
Izod Impact, Notched	0.854 J/cm @Thickness 3.17 mm	1.60 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	28.8 Âµm/m-Â°C	16.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	212 Â°C	414 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	209 Â°C	408 Â°F	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Dielectric Strength	21.7 kV/mm	550 kV/in	Method A (Short-Time); ASTM D149

Users viewing this material also viewed the following: