SABIC Innovative Plastics Cycolac® EX58F ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® EX58F ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High impact ABS for sheet extrusion and blow molding applications. FDA food contact compliant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Viscosity | 1.40e+6 cP | 1.40e+6 cP | Melt Viscosity, 240°C, 100 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 31.6 % | 31.6 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.08 GPa | 302 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 4.32 J/cm | 8.09 ft-lb/in | ASTM D256 |
| 2.99 J/cm @Temperature -30.0 °C |
5.60 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 101 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 104 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 3.20 mm |
176 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 106 °C | 223 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| Hot Wire Ignition, HWI | 7.0 - 15 sec | 7.0 - 15 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min | UL 746A |
Users viewing this material also viewed the following:
- Total Lacqtene® 2001 PBK 44 HDPE pipe (discontinued **)
- A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound
- Plenco 7500 Phenolic, Granular, Compression Molded
- Westlake 1185 PVC
- CMW® D510F Silver Nickel Contact Material ASTM B693
- ChevronTexaco Drive Train Fluid HD, SAE 60
- Ashley Polymers Ashlene® 830L-25G Nylon 6, 25% Glass Reinforced
- Ravago Manufacturing Americas Echo® RPEHD BK HDPE
- ExxonMobil Mobil 1 75W-140 Gear Lubricant LS
- Braskem CP 286 Injection Molding Polypropylene Heterophasic Copolymer
Copyright © lookpolymers.com All Rights Reserved