Cossa Polimeri ESTALUX 5513 Methyl Methacrylate Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylic (PMMA) |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTALUX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTALUX 5513 Methyl Methacrylate Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Plastic blend that combines impact properties of ABS with the excellent transparency of PMMAInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 2577 |
| Melt Flow | 13 g/10 min @Load 10.0 kg, Temperature 220 °C |
13 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched | 0.0850 J/cm @Temperature 23.0 °C |
0.159 ft-lb/in @Temperature 73.4 °F |
ISO 180/A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 93.0 °C @Load 5.10 kg |
199 °F @Load 11.2 lb |
120°C/hr; ISO 306 |
| 102 °C @Load 1.02 kg |
216 °F @Load 2.25 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Dry Time | 2.00 - 4.00 hour @Temperature 70.0 °C |
2.00 - 4.00 hour @Temperature 158 °F |
Users viewing this material also viewed the following:
- PolyOne Edgetek® SF-30CF/000 Polyphenylene Sulfide (PPS), Carbon Fiber Reinforced (discontinued **)
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar
- Flint Hills P5M6K-048 Random Copolymer Polypropylene
- SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East)
- Saint-Gobain COHRlastic® R10480 Soft Low Compression Set Silicone Sponge Rubber
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Hi-Sil 233 Filler
- DuPont Teijin Films Melinex® ST504 Polyester Film, 500 Gauge
- Eagle Brass 1008 Low Carbon Steel, Full Hardened
- Fainplast Compounds PM 7075 Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved