- RheTech Products FRP300-01 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black
RheTech Products FRP300-01 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FRP300-01 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 20 % | 20 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0113 cm/cm | 0.0113 in/in | ASTM D955 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C |
22 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength at Break | 26.2 MPa | 3800 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.21 GPa | 320 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 23.0 °C |
0.500 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 2.37 J | 1.75 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 191 - 199 °C | 375 - 390 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |
| Mold Temperature | 23.9 - 35.0 °C | 75.0 - 95.0 °F | |
| Drying Temperature | 51.7 - 65.6 °C | 125 - 150 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 8.27 MPa | 400 - 1200 psi | |
| Hold Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- Mallard Creek Polymers ROVENE® 4106 SBR Latex
- Materion BrushCAST® 21C High Strength Casting Alloy (As Cast)
- MetalTek MTEK 440B Martensitic Stainless Steel
- LATI Latiohm 66-05 PD01 G/20 PA66, 20% Glass Fiber Reinforced
- Solvay Chemicals Barium carbonate granular
- SABIC Innovative Plastics LNP STAT-KON KE002 Acetal Copolymer (Europe-Africa-Middle East)
- Samsung Cheil Industries Infino® TP-1002 PC, Unreinforced FR
- DuPont Performance Polymers Delrin® 525GR NC000 Acetal (POM) (Unverified Data**)
- 3M Scotch-Weld™ 1838 B/A Tan Two-Part Structural Adhesive
Copyright © lookpolymers.com All Rights Reserved