Resinlab® EP11HTFS Gray Filled Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Resinlab®
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinlab® EP11HTFS Gray Filled Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resinlab™ EP11HTFS Gray is a two part filled epoxy adhesive designed for bonding metals and plastics. It cures at room temperature to a tough, semi-rigid material. It has good wetting to most surfaces and is very thixotropic to resist running and sagging. This product gives very good vibration and impact resistance. It gives good resistance to water, salt spray, inorganic acids and bases and most organic solvents. It was especially formulated to a 1A:1B volume mix ratio for use in side-by-side dispensing cartridges and meter/mix and dispense equipment. EP11HTFS Gray will reach initial cure at room temperature within 2 – 4 hours with full cure in 24 – 48 hours. Cure time can be accelerated by the application of heat. Times and temperatures from 1 hour at 65°C to 15 minutes at 100°C are typical for most applications. Time to heat substrate must be taken into account. Cooler temperatures will also extend work time and increase cure times.Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
Part A; TM R050-16
1.28 g/cc
1.28 g/cc
Mixed; TM R050-16
1.29 g/cc
1.29 g/cc
Part B; TM R050-16
Water Absorption 0.17 %

@Time 86400 sec
0.17 %

@Time 24.0 hour
TM R050-35
Viscosity 700000 cP
700000 cP
Part B, RVT, #7, 2.5 rpm; TM R050-12
750000 cP
750000 cP
Mixed; TM R050-12
800000 cP
800000 cP
Part A, RVT, #7, 2.5 rpm; TM R050-12
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
TM R050-17
Tensile Strength at Break 48.3 MPa
7000 psi
TM R050-36
Tensile Strength, Ultimate 48.3 MPa
7000 psi
TM R050-36
Tensile Strength, Yield 24.1 MPa
3500 psi
TM R050-36
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
TM R050-36
Tensile Modulus 3.79 GPa
550 ksi
TM R050-36
Compressive Yield Strength 79.3 MPa
11500 psi
TM R050-38
Compressive Strength 138 MPa
20000 psi
Break; TM R050-38
141 MPa
20500 psi
Ultimate; TM R050-38
Compressive Modulus 3.34 GPa
485 ksi
TM R050-38
Adhesive Bond Strength 15.9 MPa
2300 psi
Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Glass Transition Temp, Tg 71.0 °C
160 °F
TM R050-25
Electrical Properties Metric English Comments
Volume Resistivity 8.00e+14 ohm-cm
8.00e+14 ohm-cm
Dielectric Constant 4.5

@Frequency 100 Hz,
Temperature 25.0 °C
4.5

@Frequency 100 Hz,
Temperature 77.0 °F
Dielectric Strength 16.1 kV/mm
410 kV/in
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 65.0 °C
2.00 hour

@Temperature 149 °F
1440 - 4320 min

@Temperature 25.0 °C
24.0 - 72.0 hour

@Temperature 77.0 °F
Pot Life 30 - 40 min
30 - 40 min
Mass: 50g; TM R050-19
Descriptive Properties Value Comments
Color Gray
Mix Ratio 1:1