- Lehmann & Voss LUVOCOM® 8-7190 High impact polyamide, with carbon fiber, toughness-modified
Lehmann & Voss LUVOCOM® 8-7190 High impact polyamide, with carbon fiber, toughness-modified
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 8-7190 High impact polyamide, with carbon fiber, toughness-modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Especially suitable at dynamic stress situations.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low waterabsorbtion, for dimensional stable precision parts.Bearings, sleeves, sliding elements, handles, machine parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ISO 1183 |
| Water Absorption | <= 0.15 % | <= 0.15 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 195 MPa | 28300 psi | |
| Elongation at Yield | 2.3 % | 2.3 % | |
| 2.6 % | 2.6 % | flexural | |
| Modulus of Elasticity | 19.0 GPa | 2760 ksi | |
| Flexural Strength | 260 MPa | 37700 psi | |
| Flexural Modulus | 15.0 GPa | 2180 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C | 8.89 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.500 W/m-K | 3.47 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 220 °C | 428 °F | short term |
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 295 °C | 536 - 563 °F | |
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 275 - 285 °C | 527 - 545 °F | |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- PolyOne Versollan™ OM 1262NX-9 Thermoplastic Elastomer (TPE)
- Northstar Polymers MPP-A47A Liquid Castable Polyurethane
- Johnson Matthey Mattibraze 30 Cadmium Containing Silver Brazing Alloy
- Lehmann & Voss LUVOCOM® 1/CF/40 Polyamide 66, with carbon fiber, heat stabilized
- Saint-Gobain Norton® FEP Fluoropolymer Film
- A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
- EMS-Grivory Grivory® XE 4180 nat PA1010
- DayGlo ZQ Pigments ZQ-21 Corona Magenta
- Ensinger HYDEX® 4101L Polybutylene Terephthalate (PBT)
Copyright © lookpolymers.com All Rights Reserved