Styron EMERGEâ„¢ 4310-10 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 4310-10 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ PC 4310-10 advanced resin is high-performance polycarbonate resin offering high heat resistance and maximum toughness. Applications: Consumer Electronics and Information Technology Equipment Computer and Business Equipment Portable Electronics Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 71.0 MPa | 10300 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm | 17.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Dart Drop, Total Energy | 87.0 J | 64.2 ft-lb | 8000 ipm; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 68.4 µm/m-°C @Temperature -40.0 - 82.2 °C |
38.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | 0.157 in, annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | 0.157 in, unannealed; ASTM D648 |
| 141 °C | 286 °F | 0.157 in, annealed; ASTM D648 | |
| Vicat Softening Point | 149 °C | 300 °F | 50°C/hr, 50N; ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.0630 in |
| HB | HB | 0.120 in | |
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60 Hz |
3.0 @Frequency 60 Hz |
ASTM D150 |
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz |
0.0010 @Frequency 60 Hz |
ASTM D150 |
| 0.0020 @Frequency 1e+6 Hz |
0.0020 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 405 Carboxylated Styrene - Butadiene Copolymer
- PolyOne Stat-Tech™ PC-08CF/000 FR V0 Polycarbonate (PC)
- Techmer ES Electrablend® ABS 03007 Stainless Steel Filled
- Styron MAGNUMâ„¢ 357 HP Acrylonitrile Butadiene Styrene (ABS) Resin
- DSM Arnitel® PL381 Polyether Ester Elastomer (European and Asian Grade)
- Momentive Performance Materials HCV Boron Nitride (BN) Powder
- A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene
- Mateck Thallium Bromoiodide TIBr-TII (KRS-5)
Copyright © lookpolymers.com All Rights Reserved