Polymer Resources PC/TP-GP2-G20 PC Polyester, Excellent Chemical Resistance, 20% Glass Filled  (Unverified

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend, Glass Reinforced , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC/TP-GP2-G20 PC Polyester, Excellent Chemical Resistance, 20% Glass Filled  (Unverified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
ASTM D955
Melt Flow 1.0 - 6.0 g/10 min
1.0 - 6.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.4 MPa
10500 psi
ASTM D638
Tensile Strength, Yield 72.4 MPa
10500 psi
ASTM D638
Flexural Strength 121 MPa
17500 psi
ASTM D790
Flexural Modulus 4.69 GPa
680 ksi
ASTM D790
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
240 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 263 - 285 °C
505 - 545 °F
Middle Barrel Temperature 268 - 291 °C
515 - 555 °F
Front Barrel Temperature 274 - 296 °C
525 - 565 °F
Melt Temperature 260 - 288 °C
500 - 550 °F
Mold Temperature 65.6 - 87.8 °C
150 - 190 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 4 - 6 hour
4 - 6 hour