Ravago Manufacturing Americas Hylon® N2000STL Nylon 6 (DAM)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N2000STL Nylon 6 (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ASTM D785 |
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 1.63 GPa | 236 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 106 µm/m-°C @Temperature 20.0 °C |
59.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 271 °C | 470 - 520 °F | |
| Mold Temperature | 60.0 - 87.8 °C | 140 - 190 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 400 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- Nyco NYGLOS® MSTPO Wollastonite
- Polymer Resources TP-G40 Polybutylene Terephthalate, 40% Glass Reinforced
- Honeywell Capran® Emblem™ 1530 PVDC-Coated Bi-Axially Oriented Nylon Film (discontinued **)
- Karina E 75800-35/1-B-AC Ivory PVC Compound
- Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
- Teknor Apex Sinvicomp SRP 5602 Polyvinyl Chloride, Rigid
- A. Schulman PP 1632-01 Polypropylene Random Copolymer
- Zeon Chemicals Nipol® DN171 Polyblend Nitrile Elastomer
- Bulk Molding Compounds BMC 2270 Mineral Filled, Glass Reinforced Polyester
Copyright © lookpolymers.com All Rights Reserved