- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Samsung Cheil Industries Starex® GR-4010 ABS, 10% Glass Filled
Samsung Cheil Industries Starex® GR-4010 ABS, 10% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® GR-4010 ABS, 10% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Material with 10% GF reinforcement with high stiffness that can be used in refrigerator vegetable boxesInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 7.8 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.8 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Ash | 9.7 % | 9.7 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength at Break | 68.6 MPa | 9950 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 72.6 MPa | 10500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.53 GPa | 512 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 98.1 MPa | 14200 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 4.02 GPa | 583 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.853 J/cm @Thickness 6.35 mm |
1.60 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.883 J/cm @Thickness 3.17 mm |
1.65 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 106 °C | 223 °F | B/50; ISO R306 |
| 108 °C | 226 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 6.00 mm |
HB @Thickness 0.0591 - 0.236 in |
Users viewing this material also viewed the following:
- Reltek BONDiT™ C-52 Bonding Agent, Adhesive and Primer
- PolyOne Stat-Tech™ AS-08CF/000 Black Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (disconti
- Overview of materials for Phenolic, Resole, Glass Fiber Filled
- Lehmann & Voss LUVOCOM® 1106-8088/RD Polyether imide, unreinforced, laser markable
- A. Schulman PP 1404-01 Polypropylene High Impact Polypropylene
- Toyobo PELPRENE™ S9001 Polyester TPE
- Covestro Makroblend® DP UT5005 Polycarbonate + PBT, Impact Grade
- ExxonMobil Escorene™ UL 00514 Ethylene Vinyl Acetate Copolymer (European Grade)
- EMS-Grivory Grivory® XE 4181 nat PA1010
Copyright © lookpolymers.com All Rights Reserved