Ravago Manufacturing Americas Hylon® N1000STHL Nylon 6/6 (DAM)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1000STHL Nylon 6/6 (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Water Absorption | 0.80 % | 0.80 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
78.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0590 in, NC |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 277 - 293 °C | 530 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 400 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- Reltek BONDiT™ B-45TH Adhesive, Sealant & Coating System
- Kleerdex Kydex® P90 Acrylic/PVC Extrusion Compound (discontinued **)
- H.C. Starck Grade KT 1 Crystalline Boron
- LG Chemical XR401 ABS, Heat Resistance
- Momentive Performance Materials FRV1106 Red Fluorosilicone Adhesive Sealant, Fuel Resistant Paste
- Spartech Polycast Poly II (Mil-P-5425) Cell Cast Acrylic
- SABIC Innovative Plastics LNP Stat-kon PE002 PA 6 (Asia Pacific)
- Chesterton 610 MT Plus Synthetic Lubricating Fluid
- Dow Corning MOLYKOTE® G-0052 FG WHITE EP BEARING GREASE
- China Tungsten YG8 Tungsten Carbide for Dies and Wear Part Making
Copyright © lookpolymers.com All Rights Reserved