Ravago Manufacturing Americas Hylex® P1310LLT Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1310LLT Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 1.20 kg, Temperature 300 °C |
11 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | 0.125 in; ASTM D256 |
| 5.34 J/cm @Temperature -30.0 °C |
10.0 ft-lb/in @Temperature -22.0 °F |
0.125in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 143 °C | 290 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.0590 in, NA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Middle Barrel Temperature | 277 - 288 °C | 530 - 550 °F | |
| Front Barrel Temperature | 282 - 299 °C | 540 - 570 °F | |
| Nozzle Temperature | 277 - 299 °C | 530 - 570 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 76.7 - 93.3 °C | 170 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Injection Pressure | 6.89 - 12.4 MPa | 1000 - 1800 psi | |
| Back Pressure | 0.483 - 1.03 MPa | 70.0 - 150 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 700 to 1200 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® X37 ABS
- LG Chemical LUPOY HR-5007AX Heat Resistant PC/ABS Alloy, Unreinforced
- Samsung Cheil Industries Starex® LX-0971 S ABS, Unreinforced Metallic-Look
- Samsung Cheil Industries Starex® SF-0950 MABS, Unreinforced Scratch Resistant
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- Chesterton ARC 5ES Rapid Repair Stick
- Eurostar Starflam AFR450B PA66, 25% Glass Fiber Reinforced, Flame Retardant, Injection Molding
- 3M 2A04 Co-Extruded Polyethylene Protective Tapes
- Braskem PD 943XP HOMO Polypropylene Homopolymer
- 3M Scotchlite™ IJ5100-10 Reflective Graphic Film
Copyright © lookpolymers.com All Rights Reserved