| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® H701.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium heat resistance, high impact strength. ,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | |
| Elongation at Yield | 2.7 % | 2.7 % | |
| Tensile Modulus | 2.15 GPa | 312 ksi | |
| Charpy Impact Unnotched | 18.0 J/cm² | 85.7 ft-lb/in² | |
| 12.0 J/cm² @Temperature -30.0 °C |
57.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.900 µm/m-°C @Temperature 20.0 °C |
0.500 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | |
| Vicat Softening Point | 104 °C | 219 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
|
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
|
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-(V15) 15 MFI UV Stabilized Polycarbonate With Release
- PolyOne Geon™ Vinyl Flexible XV3821 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kazanorgsintez 107-30 KTU-2 Polyethylene Masterbatch, Carbon Black Filled
- Latrobe Lescalloy® HY-180 VIM-VAR ; 2.01 - 4.00 thickness High Strength Alloy Steel
- Techmer ES Luriblend® POM CO TS20 Acetal
- A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
- ExxonMobil 626 Mobilgear 600 Series
- BASF Elastollan® 1175A10W Wire & Cable Grade Polyurethane Elastomer
- CEN® Electronic Material CN Polyimide Film, 3 Mil Thickness
- Overview of materials for PVC, Molded
Copyright © lookpolymers.com All Rights Reserved