EMS-Grivory Grivory® TSG-30/4 FA PA666-GF30
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSG-30/4 FA PA666-GF30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | conditioned; ISO 527-1/-2 |
| 180 MPa | 26100 psi | dry; ISO 527-1/-2 | |
| Tensile Strength, Yield | 100 MPa | 14500 psi | conditioned; ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 8.0 % | 8.0 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | conditioned; ISO 527-1/-2 |
| Tensile Modulus | 6.00 GPa | 870 ksi | conditioned; ISO 527-1/-2 |
| 9.70 GPa | 1410 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | dry; ISO 179/1eU |
| 8.00 J/cm² | 38.1 ft-lb/in² | conditioned; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 30.0 °C |
28.6 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 30.0 °C |
28.6 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | dry; ISO 179/1eA |
| 1.20 J/cm² | 5.71 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.600 J/cm² @Temperature 30.0 °C |
2.86 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| 0.700 J/cm² @Temperature 30.0 °C |
3.33 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 130 °C | 266 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | conditioned; IEC 60243-1 |
| 25.0 kV/mm | 635 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 475 V | 475 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Food contact | EU Requirements | |
| FDA | ||
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Sports & Leisure | ||
| Packaging | Medical packaging | |
| Processing | Injection Molding | |
| Water Contact | DVGW W270 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-MASK II HT Conductive Foil Tape
- PTS Trimid® N6-G13L 13% GFR Lubricated Nylon 6
- IRPC Polimaxx Polene R1760 High Density Polyethylene
- Techmer ES HiFill® PA6/6 GB36 IM1 36% Glass Bead Filler
- Chase Plastics CP Pryme® NN200STL (COND, 50% RH) Nylon 66, Super-Toughened, Internally Lubricated
- DuPont Performance Polymers Hytrel® 5556 Polyester Elastomer TPC-ET (Unverified Data**)
- Adell AR-18 Nylon 66, 40% Glass Reinforced
- Alcoa KAMA 1100 Prime Clear OPS, Sheet (discontinued **)
- Lanxess Pocan® DP 7102 000000 PBT, 30% Mineral (discontinued **)
Copyright © lookpolymers.com All Rights Reserved